YACOO：新款三元乙丙橡胶Keltan 9565Q的性能赶超天然橡胶

Search Product

Structure Search

Search

Online Support

Customer service

Advantage Products

Adefovir Dipivoxil Intermediates

2-Aminothiazole

Di-p-xylylene

5-Bromo-4-chloro-3-indolyl phosphate p-toluidine salt

N-Cyclohexyl-3-aminopropanesulfonic acid

(±)-6-Hydroxy-2,5,7,8-tetramethylchromane-2-carboxylic acid

Nitrotetrazolium blue chloride

3-(2-Spiroadamantane)-4-methoxy-4-(3-phosphoryloxy)phenyl-1,2-dioxetane

N-[2-(diethylamino)ethyl]acrylamide

POLYQUATERNIUM-1

4-(2-Hydroxyethyl)piperazine-1-ethanesulfonic acid(HEPES)

Tris

3,3',5,5'-Tetramethylbenzidine

Trometamol

Trometamol

4-BROMO-2-THIOPHENECARBOXALDEHYDE

Guanidine hydrochloride

IPTG

Guanidine isothiocyanate

Location: Industrial Info

YACOO：新款三元乙丙橡胶Keltan 9565Q的性能赶超天然橡胶

2015-07-08 来源：转载自第三方

关键词：合成橡胶；三元乙丙橡胶；天然橡胶

朗盛的化学家们研发出Keltan 9565Q以一种新工艺进一步提高了三元乙丙橡胶产品的分子量，进而实现了同天然橡胶相近的动态性能——即使在热老化之后依然如此。在今年的纽伦堡国际橡胶会议(IRC)期间的一场讲座中朗盛向听众展示了一些精选成果。对于其tandelta值——动态性能的一个衡量标准——Keltan 9565Q试样达到了与天然橡胶相近的较低水平。在100℃和120℃下老化168小时后，Keltan 9565Q在耐撕裂性和断裂伸长率方面则取得了比天然橡胶更好的成绩，这正是由于三元乙丙具有完全饱和的分子链。Keltan 9565Q的压缩变形优于传统硫化体系的天然橡胶，至少可以和热稳定天然橡胶(有效硫化体系)相提并论。除了强度、弹性和耐老化性能，疲劳寿命也是非常重要的。在IRC现场展示的研究报告显示，Keltan 9565Q的预老化样品同天然橡胶样品具有相当的使用寿命。然而，当对Keltan 9565Q的配方稍作优化后，疲劳寿命将极大改进，达到了热稳定天然橡胶混炼胶的同等水平。

“直到今天，高动态应力领域还在使用天然橡胶这一耐老化性能不佳的橡胶材料，Keltan9565Q开辟了三元乙丙橡胶在该领域的新应用。”Beelen说到。“Keltan9565Q还可以帮助延长维护周期，使发动机和组件运行速度更快，性能更强大：它们可以在较高温度下运行，减震件不会因为暴露在高温环境之下而迅速老化。”

朗盛的新材料甚至为加工过程也带来了好处。与天然橡胶相比，三元乙丙橡胶因分子链主链中不含双键而不易发生硫化返原。正如Beelen所解释的那样，“这一聚合物的指标范围窄、易于加工，加工过程也更加具有可重复性和一致性。”同时，这种合成橡胶可在较高温度下加工——这可以极大提高生产率。

来源：慧聪化工网